In order to derive the new charging algorithm which prolongs the lifetime of lithium ion batteries (LiBs), aging rates of LiBs for different phases and currents were analyzed. It was confirmed by ETM (Electro thermodynamic measurement) that ICR17335 of LiBs have 9 different phases over state of charge (SoC). Studies have shown that the phase is closely related to the aging rate enough to have a maximum difference of 2.5 times among phases. However, it was confirmed that the differences of the aging rates for different currents under 1C were insignificant. Therefore, it is difficult to derive a new charging algorithm that extends the lifetime by controling the current value according to the phase at the current condition under 1C. Further studies are required at currents above 1C to derive meaningful charging algorithms.
리튬이온 배터리의 수명을 연장하는 새로운 충전 알고리즘을 도출하기 위하여, 배터리의 위상 및 전류별 노화특성을 분석했다. 리튬이온 배터리, ICR17335가 충전상태(SoC)에 따라 총 9개의 위상이 존재함을 ETM(Electro thermodynamic measurement)을 통해 확인하였다. 연구 결과에 따르면, 위상간의 노화율의 차이가 최대 2.5배까지 나타날 정도로 위상이 노화율과 밀접한 관련이 있음을 확인하였다. 하지만, 1C 이하의 전류 조건에서 전류값에 따른 노화율의 변화는 미미한 것으로 확인되었다. 따라서 1C 이하의 전류조건에서 위상에 따라 전류값을 조절하여 수명을 연장하는 새로운 충전 알고리즘을 도출하는 것은 어렵다고 판단하였다. 보다 의미 있는 충전 알고리즘 도출을 위해서는 1C이상의 전류조건에서 추가 연구가 요구된다.