Among the high heat resistant polymers, aromatic poly(amide-imide)s have excellent thermal stability, mechanical properties with balanced processability. However they have yellow color caused by formation of charge transfer complex as a disadvantage. For overcome this, introduction of alicyclic rings could be one of solutions which reduce color of polymer film, but it decreases thermal stability. To improve the strength and overcome the weakness, we designed diamine monomer containing spirodilactam which has fastened ring structure. However, the ring was closed incompletely presumably due to the problem of reactivity, so diamine monomer containing a lactam ring on one side and a aliphatic chain on the other side was obtained. A poly(amide-imide) was prepared through polyamidation with diacid monomer having two trifluoromethyl groups symmetrically. The synthesized polymer was found to have low molecular weight because of impurities in diamine monomer and thus showed relatively low thermal stability. On the other hand, $T_g$ and CTE value was good as than expected although the molecular weight was not high enough and aliphatic chain was incorporated. A transparent polymer film with yellow color was obtained by solution casting method.
고내열성 고분자 중, 방향족 폴리(아마이드-이미드)는 뛰어난 열안정성, 기계적 특성과 더불어 적당한 가공성을 가졌지만 전하 이동 복합체가 형성되기 때문에 색을 띠는 것을 피할 수 없다. 이를 극복하기 위한 방법 중 하나인 지방족 고리의 도입은 고분자 필름의 색을 줄이지만 열안정성을 감소시킨다는 단점이 있다. 이를 보완하기 위해 묶여있는 고리 형태를 가지는 스파이로디락탐 다이아민 단량체를 설계했다. 하지만 반응성의 문제로 불완전하게 고리가 닫혀 한 쪽은 락탐 고리이지만 다른 쪽은 풀려있는 지방족 사슬을 가진 다이아민 단량체를 합성하였다. 이를 두 개의 트리플루오로메틸기를 대칭적으로 가지는 이산 단량체와 아마이드 중합을 통해 폴리(아미드-이미드)를 얻었다. 합성된 고분자는 단량체의 불순물로 인해 낮은 분자량을 갖는 것을 확인하였고 때문에 상대적으로 낮은 열적안정성을 보였다. 반면, 유리 전이 온도와 열팽창계수는 분자량이 충분히 자라지 못하고 지방족 사슬이 포함되어 있음에도 불구하고 예상보다 양호한 값을 얻었다. 도포방식으로 투명한 고분자 필름을 얻을 수 있었고 진한 노란색을 띠었다.