The silicide of the transition metal is attracting attention as a new material in the high temperature industry due to its high melting point, low density and high temperature strength. In this research, high-temperature oxidation behavior of zirconium silicide was investigated. Samples were prepared by spark plasma sintering with powder. In-situ XRD measurements were carried out for 20 h at $900^\circ C$, $1000^\circ C$, and $1100^\circ C$ air. The microstructure of samples was examined by scanning electron microscope and before and after oxidation. TEM analysis of the oxide film was also performed for in-depth analysis. The coating of zirconium silicide on the surface of the zircaloy-4 tube was performed by a laser-cladding method. TGA was used for the high temperature steam oxidation behavior of coated zircaloy-4. The results of these experiments provide data on the suitability of zirconium silicide as coating materials on the Zircaloy-4 for accident tolerance fuel cladding.
전이 금속의 규화물은 고 융점, 저밀도 및 고온 강도로 인해 고온 산업에서 새로운 재료로 주목 받고 있다. 본 연구에서는 지르코늄 실리사이드의 고온 산화 거동을 조사 하였다. 샘플은 방전 소결에 의해 준비되었다. 실시간 X선 회절 분석은 $900^\circ C$, $1000^\circ C$ 및 $1100^\circ C$ 공기 중 에서 20 시간 동안 수행되었으며, 산화 전후 샘플의 미세 구조는 주사형 전자 현미경을 이용해 조사되었다. 심층 분석을 위해 산화막의 투과 전자 현미경 분석도 수행하였다. 지르칼로이-4 관 표면의 지르코늄 실리사이드 코팅은 3-D 레이저를 이용하여 진행되었다. 코팅된 지르칼로이-4는 고온 증기 산화 거동에 연구를 위해 $1200^\circ C$ 증기/아르곤 혼합 조건에서 2000초 동안 산화 되었다. 이 실험의 결과는 사고 저항성 핵연료 피복관 개발을 위한 Zircaloy-4의 코팅 재료로서 지르코늄 실리사이드의 적합성을 평가한다.