Cholesterol-containing amphiphilic monomers, 1-ethenyl-3-(8-(cholest-5-en-3$\beta$-yloxy)-3,6-dioxaoctyl)-2-pyrrolidone (ECDP) and 1-ethenyl-3-(6-(cholest-5-en-3$\beta$-yloxy)hexyl)-2-pyrrolidone (ECHP), and cholesterol-containing amphiphilic polymers, poly(ECDP-co-N-vinylpyrrolidone) and poly(ECHP-co-N-vinylpyrrolidone), were synthesised, and their properties and suprastructures were investigated. ECDP formed vesicles in water by sonication, whereas ECHP did not. The polymerization of preformed vesicles derived from ECDP in water by water-soluble initiator resulted in the formation of polymeric vesicles of ECDP which were more stable to the addition of ethanol and tannic acid than the monomeric vesicles exhibiting higher long-term stability. The solution behaviors and the suprastructures of the cholesterol-containing amphiphilic polymers were influenced by copolymer composition and molecular weight. The polymers with low N-vinylpyrrolidone (NVP) content, apparently insoluble in water, were dispersed by sonication or by injection of organic solution into water to form vesicles. The more water-soluble polymers with high NVP content formed hydrophobic microdomains in water into which cholesterol was efficiently incorporated. The polymers underwent morphological change as cholesterol was solubilized and discrete lamellar bilayers were observed by electron microscope. Thus formed bilayers were considered to be responsible for the efficient cholesterol solubilization of the amphiphilic polymers. Some resemblances to certain biological membrane systems were found in the present solubilization systems.
콜레스테롤을 포함하는 양친매성 단량체인 1-에테닐-3-(8-(콜레스트-5-엔-3-$\beta$-일옥시)-3-6-다이옥사옥틸)-2-피롤리돈 (ECDP) 및 1-에테닐-3-(8-(콜레스트-5-엔-3-$\beta$-일옥시)헥실)-2-피롤리돈 (ECHP)과 콜레스테롤을 포함하는 양친매성 고분자로서 폴리(ECDP-N-비닐피롤리돈) 및 폴리(ECDP-N-비닐피롤리돈)을 합성하였고, 이들의 성질과 초구조에 대해서 연구하였다. ECDP는 초음파의 조사에 의하여 물속에서 베시클을 형성하였으나 ECHP의 경우는 물속에서의 분산이 불가능하였다. 물속에 형성된 베시클을 수용성 개시제로 중합하여 ECDP의 중합된 베시클을 얻었는데, 이 중합된 베시클은 중합되지 않은 것보다 오랜 기간 동안 안정할 뿐만 아니라 에탄올이나 탄닌산의 첨가에도 우수한 안정성을 보였다. 공중합체의 구성비와 분자량은 콜레스테롤을 포함한 양친매성 고분자의 용액 성질과 초구조에 영향을 미쳤다. N-비닐피롤리돈 (NVP)의 함량이 적은 고분자는 물에 녹지 않는 것처럼 보이지만 초음파의 조사에 의해서 물속에 분산되어 베시클을 형성하였다. NVP의 함량이 많아 수용성이 증가된 고분자는 물속에서 비수용성 미세영역을 형성하는데 이 미세영역에는 콜레스테롤이 효과적으로 삽입되었다. 콜레스테롤이 고분자의 미세영역속에 녹아들어감에 따라서 이 고분자의 형태가 변하였는데 전자현미경에 의해서 라멜라 형태의 이중막이 명확히 관찰되었다. 이중막의 형성 때문에 효과적인 콜레스테롤의 용해가 가능 하였다고 여겨지며 이러한 용해 체계는 생체 유사성을 보인다.