Many organic polymer research groups have studied PPV and its derivatives. We synthesized crosslinked conjugated conducting polymer via water soluble precursor route. 1,2,4,5-Tetramethylbenzene crosslinked conjugated polymer and copolymers with poly(2,5-dimethoxyphenylene vinylene) unit were characterized by thermogravimetry(TGA, DSC), NMR, IR and UV-VIS spectrophotometry. The actual compositions of the copolymers were determined by elemental analysis. Homo film was brittle and it was not stretched. It was undopable with $I_2$ but the maximum conductivity of $FeCl_3$ doped homo film was $2.90\times10^{-6}$ (S/cm). Copolymers were not nearly stretched. They showed maximum conductivities of 33.47 (S/cm) and 68.33 (S/cm) respectively, when doped with $I_2$ and $FeCl_3$. As the contents of tetramethylbenzene units increased, the maximum conductivity of copolymers decreased. In contrast to the copolymers with PDMPV, copolymers with PPV were stretched very well and showed the maximum conductivity of $4.8\times10^{-2}$ (S/cm), when doped with $I_2$.
PPV와 그 유도체의 합성은 여러 그룹에서 활발하게 연구하고 있다. 본 연구에서는 한 방향으로 공액 이중 결합된 PPV와 달리 공액이중 결합으로 크로스링킹된 전기 전도성 고분자를 물에 녹는 선중합체를 거쳐 합성하였다. 합성된 중합체와 PDMPV와의 공중합체들을 열분석 (TGA,DSC)과 IR 및 UV-VIS 분석을 통하여 기본적인 특성을 알았으며, 원소 분석을 실행하여 공중합체의 실제 조성비를 밝혔다.
PPV와 달리 단독 중합체 필름은 잘 부스러지며, 연신도 안 되었다. 약한 산화제인 $I_2$ 도핑은 거의 되지 않았으나 $FeCl_3$ 도핑에 의해 $2.90\times10^{-6}$ (S/cm)의 값을 얻었다. 공중합체들 또한 거의 연신이 안되었다. 공중합체는 $I_2$ 도핑에 의해 최고 33.47 (S/cm)의 값을 얻었으며, $FeCl_3$ 도핑에 의하여 68.33 (S/cm)의 최고 값을 얻었다. 테트라메틸벤젠 유니트의 양이 많을 수록 공중합체의 전도성은 감소하였다. PDMPV와의 공중합체와 달리 PPV와의 공중합체는 연신이 잘 되었고, 도핑에 의해 $4.8\times10^{-2}$ (S/cm) 의 값을 보였다.