Recently, $Pt_3M$ (M=Fe,Ni,Co,Cu…) intermetallic compounds are being spotlighted as candidates for ORR catalysts. To form intermetallic compound, high temperature is required, but particles are aggregated in this process. In this study, we prevented particle aggregation by carbon coating. As a result, ECSA was almost maintained $(37.6 → 33.3 m^2/g)$ and $Pt_3Fe$ structure was formed. $Pt_3Fe/C$ exhibited $0.454 m^2/g$ in initial mass activity. After ADT 8,000 cycles, there wasn’t serious particle aggregation and composition was maintained. As a result, $Pt^3Fe/C$ exhibited $0.343 m^2/g$ in mass activity, after ADT 8,000 cycles. We suggested $Pt_3M$ intermetallic compounds are good candidates for the most active and durable ORR catalysts.
최근, $Pt_3M$ (M=Fe,Ni,Co,Cu…) 형태의 금속간 화합물은 높은 활성과 좋은 내구성으로 인하여 산소환원반응 촉매로 주목받고 있다. 이러한 금속간 화합물을 만들기 위해서는 고온에서의 열처리가 필요한데, 그 과정에서 입자가 뭉쳐 좋은 촉매특성을 갖기 어렵다. 본 연구에서는, 이를 극복하고자, 열처리 전 카본물질로 코팅하여 입자가 뭉치는 것을 방지하였다. 그 결과, 표면적 감소를 최소로 하여 $(ECSA: 37.6 → 33.3 m^2/g)$, $Pt_3M$ 구조를 만들 수 있었다. 특성을 평가 결과, $0.454 m^2/g$ 의 준수한 mass activity를 갖는 것을 확인하였다. 내구성 평가를 위해 ADT (Accelerated Durability Test) 를 진행하였고, 8,000 cycle 이후에도, ECSA가 대부분 유지 되었고, 조성도 대부분 유지되는 것을 확인하였다. 그 결과 8,000 cycle 이후, $0.343 m^2/g$ 의 준수한 mass activity를 갖는 것을 확인하였으며, 이러한 금속간 화합물의 경우, 산소환원반응에 있어, 고 활성, 고 내구성의 우수한 촉매가 될 수 있음을 제시하였다.