Cyclopolymerization of 2.2-dimethyl-5.5-dipropargyl-4.6-diketo-1.3-dioxane was done by group 5 and 6 transition metal systems. $MoCl_5$ alone more effectively polymerized than $WCl_6$ alone. The polymer yield by $MoCl_5$-based catalysts used cocatalysts were decreased than $MoCl_5$ alone.
Polymer structure was identified by $^1H-NMR$, $^{13}C-NMR$, IR, and UV-visible spectroscopy. From these spectroscopic results, poly(DPIPM) has conjugated polyene backbone containing six-membered cyclic structure. Poly (DPIPM) has only partially soluble in general organic solvent but excellent oxidative stability in air. The thermal properties were also studied. The electrical conductivity, $\sigma$, rises from the undopped level of $10^{-11}$S/cm to a maximum value $10^{-11}$S/cm to a maximum value $10^{-3}$S/cm for $I_2$ dopping.
본 논문에서는 합성된 폴리머의 구조확인 및 물리적 특성등을 연구하였다. 디프로파길이소프로필리덴말로네이트는 전이금속촉매로 중합시킨결과 공액이중 결합을 주측쇄로 가지는 육각형의 고리화반응이 일어났다. 이는 $^1H$ NMR, $^{13}C$ NMR, IR, UV-Visble등으로 확인하였다. 또한 조촉매로 유기알루미늄과 유기틴계 화합물을 사용하였는데 특히 유기틴계 화합물($ph_4sn$)이 상당한 조촉매 효과를 나타내었다. 폴리디프로파길이소말로네이트는 일반적인 유기용매에 50%정도 녹는것으로보아 일부 폴리머들은 cross-linking이 일어나는것으로 예측이되며 열중량분석으로 합성된 폴리머의 열적성질을 조사하였다.
또한 IR로부터 공기에대한 산화안정성이 상당히 좋음을 알 수 있었다.
전기전도성은 $10^{-11}$S/cm 에서 도핑했을경우 $10^{-3}$S/cm 정도였다.