4,4-diphenoxy-1,6-heptadiyne was prepared by a Grignard reagent of propargyl bromide with dichloro-diphenoxy methane. Polymerization was attempted by $MoCl_5$ and $WCl_6$ associated with cocatalyst such as organotin and organoaluminium compounds. A moiybdenium catalyst was found to be a particularly effective catalyst for the cyclopolymerization of 4,4-diphenoxy- 1,6heptadiyne. Polymerization of 4,4-diphenoxy-1,6-heptadiyne by various catalysts leads to a violet solid ($\overline{Mn}=52000$), soluble in common organic solvents. The structure of polymer was identified by $^1H$-NMR, $^{13}C$-NMR, IR and UV-Vis spectroscopies. From these spectroscopic results, poly(DPHD)s possess polyene structures having cyclic recurring units in the polymer backbone. The poly(DPHD) has excellent properties in both the solubility in general organic solvent and the oxidation stability identified from IR spectra. The electrical conductivity is $10^{-3}$s/cm for $I_2$ doping.
본 논문에서는 4,4-다이페녹시-1,6-헵타다이아인의 합성과 이 모노머에 전이 금속 촉매를 사용하여 중합시킨 연구내용을 다루었다. 4,4-다이페녹시-1,6-헵타다이아인의 합성은 Grignard 반응을 통해 합성하였다. 중합 촉매로서는 $WCl_6$ 와 $MoCl_5$ 를 사용하였고, 유기틴계 화합물과 유기알루미늄계 화합물을 조촉매로 사용하였다. 폴리-(4,4-다이페녹시-1,6-헵타다이아인)은 산화에 대한 안정성, 유기 용매에 대한 용해도에 있어서 우수한 물성을 나타내었다.
$^1H$-NMR과 $^{13}C$-NMR, IR, UV-Vis 스펙트럼들로부터 합성한 중합체가 공액 이중 결합을 가지며 고리화된 구조를 하고 있는것으로 추정 되었다. 폴리-(4,4-다이페녹시-1,6-헵타다이아인)에 도핑시켰을때 전기전도도는 $10^{-3}$ s/cm의 값을 나타내었다.