The polymerization of 4,4-diphenyl-1,6-heptadiyne was done by various transition metal catalyst system. The resulting polymer has conjugated polyene backbone containing six-membered cyclic structure. The poly(4,4-diphenyl-1,6-heptadiyne) has excellent properties in both the solubility in general organic solvent and the oxidation stability identified from IR spectra. Therefore, the resulting polymer films were easily obtained by casting with organic solvent. The thermal properties and the morphology of poly(4,4-diphenyl-1, 6-heptadiyne) films were also studied. The electrical conductivity and the magnetical properties of resulting polymer upon doping were chainged. The changes in IR, UV-Visible, morphology ESR spectra, and the activation energy of the conduction by doping were also researched.
본 논문에서는 비 공명구조의 4,4-다이페닐-1,6-헵타다이아인을 5족, 6족 전이금속 촉매를 사용하여 중합시켜 공명구조의 육원 고리 형태를 갖는 폴리(4,4-다이페닐-1,6-헵타다이아인)을 합성하였다. 중합에 있어서 조촉매로 유기 알루미늄계와 유기틴계 화합물을 사용하였다. 폴리(4,4-다이페닐-1,6-헵타다이아인)은 산화 안정성, 유기용매에 대한 용해도에 있어서 우수한 물성을 나타내며 모폴로지 연구결과 폴리아세틸렌에서 볼 수 있는 섬유상이 보여졌다. 폴리 (4,4-다이페닐-1,6-헵타다이아인)은 깊슨 그룹에의해 합성된 폴리(1,6-헵타다이아인)에 비해 전기전도성이 백배 정도 떨어지며 가시광선 영역의 스펙트럼에서 100 nm 정도 청색이동 했음을 볼 수 있었다. 이것은 치환기 도입에 의해 좀 더 꼬여진 나선형 구조가 되면서 공액 폴리엔을 따라 파이 전자 밀도의 전달이 어려워지기 때문이다. 전자스핀 공명을 이용하여 폴리(4,4-다이페닐-1,6-헵타다이아인)의 스핀이 도핑에 따라 스핀 밀도가 증가하여 선나비 $(\Delta H_{pp})$ 가 감소됨을 볼 수 있었다. 이것은 전자의 자유로운 움직임 정도와 비대칭적인 폴리머 구조로부터 기인한다.