The present study has attempted to elucidate the causes of the hydrogen evolution enhanced by the wear process. In this work an open wear-producing system was developed: wear process and hydrogen measuring process were separated from each other, and each process worked successively. The real hydrogen evolution from the specimen exposed to the wear process ocurred more than that from the unexposed specimen even in consideration of the amount of hydrogen both mechanically detached and trapped to the structural defects. The amount of hydrogen evolved due to the wear process was increased with both the time exposed to wear process and the applied normal stress in the wear process. Hydrogen evolution enhanced by the wear process was discussed in terms of the amount of hydrogen evolved as a function of normal stress and the time exposed to the wear process, suggesting that the dislocations generated by the wear process cause the retardation of the hydrogen diffusion due to the trapping of hydrogen in the initial stage of the wear process and the acceleration of the hydrogen diffusion in the later stage where dislocation trap sites are filled with hydrogen to a fixed level.
본 연구는 마모 유기 수소 방출 현상의 원인을 규명하기 위하여 수행되었다. 본 연구에서는 개방 마모 발생계가 채택되었는 바, 마모 과정과 수소 방출 측정이 분리되어 연속적으로 실행되었다. 마모 과정에 노출된 시편에서 마모 동안에 방출된 수소량이, 기계적으로 분리된 수소와 시편 내에 trap된 수소량을 고려하더라도, 마모 과정에 노출되지 않은 시편에서보다 더 많음을 알 수 있었다. 또한 마모 과정 동안에 방출되는 수소량은 마모 시간과 마모 중량이 증가함에 따라 함께 증가하였다. 이러한 마모 유기 수소 방출 현상의 원인을 고찰하여 본 결과 마모 초기 과정에서는 생성된 전위가 수소를 trap하여 수소의 확산을 억제하는데 기여하게 되고, 그 뒤에 이러한 trap들이 일정한 수준 이상으로 채워진 후엔 이러한 전위 조직이 수소의 확산의 통로가 되어서 오히려 수소의 방출을 돕는 것으로 여겨진다.