Two epoxy resins were synthesized by glycidylation of two diamino compounds 3,3'-and 4,4'-diaminodiphenyl sulfone (DDS) and spectroscopically characterized. The resins prepared were then cured with curing agent of 3,3'-DDS, 4,4'-DDS and 4,4'-diaminodiphenyl methane (DDM).
For the curing reactions cure kinetics was investigated by measuring enthalphy changes at constant temperature of 140℃, 170℃ and 200℃.
In order to study an effect of curing agent content upon the Tg values, the epoxy resins containing various amounts of curing agents were cured for one hour at 140℃ and then for 5 hours at 170℃, and the Tg values of the cured epoxy resins were determined.
These Tg changes with curing agent content were discussed and compared with the DDM-derived epoxy resin/4,4-DDS system which is very widely applied in carbon fiber prepreg industry.
에피클로로히드린을 3,3'-디아미노디페닐설폰 (3,3'-DDS) 또는 4,4'-디아미노디페닐설폰 (4,4'-DDS)과 반응시켜 두 종류의 수지를 얻어 각종 스펙트럼과 크로마토그램, 에폭시 당량으로 구조를 밝혔다.
제조된 수지를 3,3'-DDS, 4,4'-DDS, DDM등의 아민계 경화체로 경화 시킬때의 경화 속도를 140℃, 170℃ 및 200℃에서 DSC를 이용하여 고찰하였다.
이들 두 수지를 세 종류의 아민으로 경화 시켜 Tg를 측정했다.
3,3'-DDS 수지/3,3'-DDS, 3,3'-DDS 수지/4,4'-DDS, 4,4'-DDS 수지/3,3'-DDS와 같은 경화체계에서의 Tg는 경화제의 분율이 커질수록 떨어지는 경향을 보이고 4,4'-DDM 수지/DDM, 3,3'-DDM 수지/DDM의 경우는 Tg가 보다 빨리 떨어진다.
또한 세 경화제중 4,4'-DDS를 사용했을때의 Tg가 가장 높았으며 DDM이 가장 낮은 Tg를 보였다.