The swelling and stress-elongation experiments have been performed for two kinds of tactic poly (2-hydroxyethyl methacrylate) (P-HEMA) with varying crosslinker concentrations.
Isotactic and syndiotactic P-HEMA gels are swollen in aqueous salt solutions varying molal concentrations. The solute which we used are NaCl, $MgCl_2$, $Na_2SO_4$, $MgSO_4$ and urea. The water content and salt partition coefficient were determined. And stress-elongation curves of the gels are obtained. From these results, the effective number of chain ($υ\mid_e$) and the Flory-Huggins interaction parameter ($χ\mid_1$) are also obtained.
The swelling experiment performed also varying solvents, and the degree of swelling is determined. The solubility parameter of P-HEMA is obtained as 13.6 using the correlation between the degree of swelling and the solubility parameter ($δ\mid_1$) of solvents.
The mechanical properties of syndiotactic P-HEMA is stronger than that of isotactic P-HEMA, and the water contents of both gels become smaller when the crosslinking increases. This water content of isotactic P-HEMA is more than that of syndiotactic P-HEMA.
수화겔의 팽윤현상과 역학적 성질은 여러가지 실험결과와 이론적인 고찰로서 연구되고 있다.
본 연구에서는 두가지의 규칙성 폴리-2-히드록시 에틸 메타크리레이트를 사용하여 수화겔 속의 물의 함량과 응력 -신장 도표를 얻고, 여러가지 용매에 대한 팽윤도를 조사하였다.
수화겔 속의 물의 함량은 여러가지 몰랄 농도를 가진 염의 수용액에서 얻어졌는데, 이 염들에 대한 분배계수도 함께 측정되었다. 이때 사용되어진 염들은 NaCl, $MgCl_2$, $Na_2SO_4$, $MgSO_4$ 그리고 urea 였다. 이 실험 결과와 응력-신장 도표로부터 폴리머 사슬의 유효갯수 ($υ_e$) 그리고 Flory-Huggins의 상호작용 계수 ($x_1$)이 얻어졌다.
이 규칙성 수화겔의 여러가지 용매에 대한 팽윤도도 측정되었는데, 팽윤도와 용해계수 ($δ_1$)과의 관계로부터 P-HEMA의 용해계수가 13.6 을 알아냈다.
위와 같은 여러 실험 결과를 고찰하면, 이 수화겔의 역학적 성질은 isotactic보다 syndiotactic이 더 강하며 가교제가 많이 첨가될수록 강한 것으로 나타났다. 그리고 물의 함량은 syndiotactic보다 isotactic이 더 많으며 가교제의 증가와는 반비례하는 관계를 얻을 수 있다.