The aqueous polymerization of acrylamide with $H_5IO_6-MnCl_2$ initiator was studied under deserated condition at the temperature range of $30^\circ-40^\circC$
High molecular weight polymer was obtained. And the addition of permanganate greatly reduced the induction period as well as molecular weight. It was considered that the formation of permanganate participates in polymerization.
From the obtained results, the rate of polymerization was given by the emipirical rate expression $Rp=K[monomer]^{1.17}[H_5IO_6]^{0.58}[MnCl_2]^{0.55}$. Activation energy was found to be 20.0 Kcal/mole at the temperature range of 30˚-40℃. And the catalytic effect of metal compounds ($MnCl_2$, $CoCl_2$, $FeCl_2$) was investigated. It make clear that $MnCl_2$ gave the highest catalytic effect; $CoCl_2$ showed the good catalytic effect; $FeCl_2$ showed the least catalytic effect.
It is proposed that the polymerization of acrylamide with $H_5IO_6-MnCl_2$ is proceeded by the radical mechanism.
$H_5IO_6-MnCl_2$ 의 개시제를 사용해서 acrylamide 를 온도범위 ($30^\circ-40^\circC$)에서 수용성 중합을 시켜 분자량이 큰 중합체를 얻었다.
온도, 농도, 시간등을 변화시키면서 중합시켰다. 온도, 중합시간과 개시제의 농도가 증가할수록 중합수율이 증가하였지만, 개시 유도시간이 줄었다.
이러한 결과로부터 permanganate 의 생성속도가 중합속도에 상당히 관여함을 알 수 있었다.
또한 중합 금지제인 benzoquinone 를 첨가하면 중합속도와 중합수율이 현저히 떨어졌다.
이 결과로부터 라디칼 중합과정임을 알수 있다.
그리고 여러 전위금속에 대한 촉매효과를 조사하였으며, 이때 $MnCl_2$ 가 가장 좋은 촉매효과를 가졌고, $CoCl_2$ 도 촉매효과를 나타냈고, $FeCl_2$ 는 거의 촉매효과가 없음을 알았다.