Acoustic emission (AE) release in zinc polycrystals has been studied in air, glycerin, and silicon oil environments on the same testing condition with large(L) and small(S) specimens.
Total AE energy release increased rapidly up to the critical strain (0.16 and 0.15 for L and S specimens respectively), then further increase was minimal. Generally this variation shows the same behavior as yielding and work-hardening curve. However, the behavior of total AE energy with strain showed quite irrelevant to the stress-strain curve.
The analysis of the accumulated peak amplitude distribution and the accumulated event energy spectra showed that the rapid increase up to the critical strain was caused by release of high amplitude AE signals, whereas the low amplitude emissions was dominant beyond this critical strain.
The influence of environments on the AE energy release, firstly studied in the present work, showed that the magnitude of energy release was observed in the sequence of air, glycerin, and silicon oil environments.
The greater emission energy observed during plastic deformation of zinc polycrystals in glycerin environment than in silicon oil environment, in spite of its greater density and viscosity in glycerin environment, is explained in terms of the ratio of the density to the coefficient of viscosity and the rate of diffusing.
Zn 다 결정이 소성변형될 때 발생하는 Acoustic Emission (AE) 에 공기, 글리세린, 실리콘 오일의 환경들이 미치는 영향을 큰 시편과 작은 시편에 대하여 같은 실험 조건하에서 연구 되었다.
총 AE 에너지 방출은 임계변형 (큰 시편과 작은 시편에 대하여 각각 0.16 과 0.15)까지 급격히 증가하고, 그 이상의 변형에서는 미소한 증가를 보였다. 일반적으로 변형에 대한 총 AE 에너지 방출은 항복곡선과 가공 경화곡선에 거의 같은 현상을 보이나, 응력-변형곡선에 대해서는 큰 관계를 볼 수 없다.
누적 최대 진폭 분포와 누적 사건 에너지 스펙트라의 분석에 의하면, 임계변형까지의 급격한 총 AE 에너지 증가는 큰 진폭의 AE 방출에 의한 것이고 임계변형 이후에는 작은 진폭의 AE 방출이 대부분이었다.
본 논문에서 처음으로 행하여진, 환경의 영향을 받은 AE 에너지 방출량은 공기, 글리세린, 실리콘 오일의 환경 순으로 나타났다.
Zn다 결정이 소성변형될 때, 글리세린의 밀도와 점도가 실리콘 오일보다 큼에도 불구하고, 실리콘 오일 환경보다 글리세린 환경에서 보다 많이 측정된 AE 에너지는 환경의 밀도와 점도의 비 그리고 시간에 따른 분산량에 의하여 설명 되었다.