The effect of ion nitriding on mechanical properties of STD 11 steel was studied. Surface hardness, core hardness, thickness of nitrided layer, impact strength, and wear volume of nitrided Cr-Mo-V steel were measured varying the nitriding time and temperature. The effect of tempering temperature before ion-nitriding was investigated.
The thickness of compound layer and diffusion layer increased with both the nitriding time and the nitriding temperature. The thickness of the nitrided layer was found to be thinner than that of other nitralloy or nitriding steel because of high chromium content. Maximum surface hardness of 1400 Hv was obtained after 10 hr nitriding at 450℃. Lowest impact strength was obtained when treated at 450℃ and it seemed relatively independent of the nitriding treatment time. The wear rate tended to be smaller for thicker compound layer.
本 실험에서는 Cr-MO-V 系의 STD 11 냉간 가공용 공구강의 질화처리가 충격강도, 마모특성에 미치는 영향을 주로 연구하였고 처리온도와 처리시간이 STD 11 鋼의 표면경도, 芯部경도, 질화층의 깊이, 충격강도 및 내마모성등에 미치는 영향과, 담금질 후에 뜨임온도가 질화후에 나타내는 효과에 대해 고찰하였다.
질화온도와 질화시간이 증가하면, 합성층과 확산층이 증가되나, Cr의 함유량이 높기 때문에 질화층의 깊이는 일반 질화강에 비해 낮았고, 450℃ 10시간 처리에서 표면경도를 1400Hv까지 증가 시킬 수 있었다. 충격강도는 450℃에서의 질화처리 때 가장 낮았고, 질화시간에 의한 영향은 비교적 적은 것으로 보였고, 합성층의 증가에 따라 내마모성은 증가되었다.
실험 중에 관찰된 바에 의하면, 질화시의 전원공급 방식은, sputtering 과정을 지나 안정된 glow 상태에 도달하면 완전직류에 의한 질화도 가능하다는 점을 관찰하였다.