Stress corrosion behavior of type-304 austenitic stainless steel in 45.5 wt. % $MgCl_2$ solution was studied with U-bend specimen between 125℃ to 155℃ solution temperature.
Maximum crack depth increased logarithmically with the increase of time exposed to solution at various temperatures. From maximum crack depth measurement, induction period before cracking and crack propagation period were evaluated. The result indicated that these periods decreased with the increasing corrosive solution temperature. Apparent activation energy obtained from Arrhenius equation showed that the apparent activation energy for induction period was larger than that for crack propagation period.
This study emphasizes the importance of corrosive solution temperature in constant strain.
45.5 wt.% $MgCℓ_2$ 용액내에서 type-304 austenitic stainless 강의 응력부식거동을 U - bend 시편으로 125℃로 부터 155℃ 까지 용액온도를 변화시켜 연구하였다.
각 온도에서 최대 crack 깊이는 용액에 잠겨 있는 시간이 증가함에 따라 logarithm 함수로 증가하였다.
최대 crack깊이 측정으로 부터 cracking전의 유도기간과 crack전파기간을 구하였다. 이들 기간은 부식용액의 온도가 증가함에 따라 감소하였다.
Arrhenius식으로 부터 구해진 겉보기 활성화 energy 로 부터 유도기간에 대한 겉보기 활성화 energy 값이 crack 전파기간에 대한 겉보기 활성화 energy 값보다 큰 것으로 나타났다.
본 연구는 일정신연을 가한 경우 부식용액의 온도의 중요성을 강조하고 있다.