It is observed that there are at least four adsorbed species of oxygen on zinc oxide. When oxygen is adsorbed at room temperature, two adsorbed species are formed. One is $O^-_2$ and it consists 90% of the adsorbed oxygen. It shows two absorption line at g=2.04 and g=2.01 in E.P.R. spectrum.
When temperature is raised in vacuum, some of it desorbs and rest is changed to $O^-$.
It shows desorption peak at 190℃ in T.P.D. spectrum and reacts readily with propylene at room temperature.
Another kind of adsorbed oxygen shows one absortion line at g=2.003 in E.P.R. spectrum.
It does not react with propylene at room temperature.
When oxygen is adsorbed at 220℃, $O^-$ is mainly formed and it shows desorption peak at 280℃ in T.P.D. spectrum.
When oxygen is absorbed at above 300℃, $O^-$ is formed.
It shows no absorption peak in E.P.R. spectrum and desorbs at 430℃ in T.P.D. spectrum.
External electric field increased or decreased the amount of the adsorbed oxygen according to the boundary layer theory and field induced transformation of adsorbed oxygen from one form to another seems to occur too.
산화아연에 흡착된 산소의 종류는 적어도 4가지가 있으며 온도의 변화에 따라 흡착종 상호간의 변화가 관찰되었다.
실온에서 흡착된 산소는 2가지 흡착종을 생성하였다. 이중 90% 가량은 $O^-_2$ 로 E.P.R. 스펙트럼에서 g = 2.04 g = 2.01에 넓은 흡수 봉우리를 가지고 있으며 온도가 올라감에 따라 탈착과 함께 $O^-$로 변화하였으며 T.P.D. 스펙트럼에서는 190℃에서 탈착 봉우리를 보여 주었고 실온에서 프로필렌과 곧 반응하였다.
나머지 10%를 차지하고 있는 흡착종은 EPR 스펙트럼에서 g=2.003에 흡수 봉우리를 보여 주었으며 실온에서 프로필렌과 반응하지 않고 T.P.D. 스펙트럼에서 100℃부근에 탈착 봉우리를 보여준다. 220℃에서 흡착한 산소는 주로 $O^-$로 존재하였으며 T.P.D. 스펙트럼에서 280℃에 탈착 봉우리를 가지고 있으며 E.P.R. 스펙트럼에는 g = 2.003에 흡수 봉우리를 가지고 있다.
그리고 E.P.R.에는 반응하지 않지만 T.P.D. 스펙트럼에서 430℃에 탈착 봉우리를 보여주는 흡착종이 있는데 이것은 $O^=$ 이다. 외부의 전장은 boundary layer theory에 따라서 산소의 흡착을 제어하지만 전장에 의해서 흡착종의 변화가 같이 일어나는것 같다.