The changes of preferred orientation and mechanical properties of sand-cast Mg-9tw% al-(0,1,2,3)wt% Zn alloys were investigated by heat treatment.
The specimens were heat treated by the solution heat treatment and two different methods of aging at the temperature range of 175℃-250℃.
The results indicate that the preferred orientation is [0001] at the parallel direction and [1010] and [1120] at the normal direction to he end plane of cast plate after solution heat treatment.
Preferred orientation is not changed by Zn content in alloys and aging times.
The stage of precipitation of this system is followed by the incubation period, main precipitation and slow attainment of equilibrium stage.
The main precipitation rate increases at high aging temperature but is not affected by the Zn content of the alloy.
The results of microhardness data indicate that the discontinious precipitation occurs more rapidly than the continious precipitation and occurs rapidly in higher Zn content, and the continuous precipitation largely affects the mechanical properties of this system.
On aging the alloy containing 2Wt% Zn has a most improved tensile strength of this system, and the tensile strength of alloys containing 1-2Wt% Zn remarkably improve by double aging followed 100℃ preaging.
사형 주조된 Mg-9wt% Aℓ-(0,1,2,3)wt% Zn 합금들의 우선 배향과 기계적 성질들의 변화가 열처리에 의해 연구되었다.
시편들은 용체화처리와 175℃ - 250℃의 온도 범위에서 두 가지 다른 시효 처리 방법에 의해 열처리 되었다.
그 결과들은 용체화 처리 후 우선 배향이 주조된 판재의 끝면에 대해 평행한 방향에서는 [0001]이 강해지고, 수직한 방향에서는 [1010]과 $[11\bar{2}0]$이 강해지고 있음을 보이고 있다.
우선 배향은 그 합금의 Zinc의 양과 시효 시간에 따라서는 변화되지 않는다.
이 계의 석출 단계는 잠복기, 주석출기, 평형기의 세 단계로 나타나며 시효 온도가 높을수록 주석출이 빠르게 되나 Zinc의 양은 주석출에 크게 영향을 미치지 않는다.
미소 경도의 결과는 discontinuous precipitation이 continuous precipitation보다 빨리 일어나며, Zinc의 양이 많아질수록 discontinuous precipitation이 빨라지고, continuous precipitation이 이 계의 기계적 성질을 지배하고 있음을 보인다.
2wt% Zinc를 포함하는 합금이 이 계에서 시효 처리시 그 인장 강도가 가장 높으며, 1 ~ 2 wt%의 Zinc를 포함하는 합금은 100℃의 preaging후 double aging에 의해 그 인장 강도가 현저히 증가하고 있다.