As the difunctional compounds and vinyl compounds containing an ionic bonds in the molecule, divalent metal salts of p-hydroxy benzoic acid and maleic acid were prepared in high purity and high yield.
Mg, Ca and Cu elements were selected as the divalent metals.
◁수식 삽입▷(원문을 참조하세요)
Metal containing polyurethanes which involve ionic linkages in the main chain were synthesized by the addition polymerization reaction of (Ⅰ) or (Ⅰ) and ethylene glycol with diphenyl methane diisocyanate.
It was found that the viscositiy of the polyurethane was decreased markedly with increasing metal contents. It was also observed that the melting point was lowered as incoorporated metal ion into polyurethane.
The copolymer of (Ⅱ) and acrylonitrile (A.N) were also copolymerized and characterized.
It was observed that the viscosity of the copolymers were increased greately with increasing the content of metal ions. It was indicated that the melting point was dropped as (Ⅱ) was incooporated into the polymer.
분자내에 금속염을 포함한 이온결합을 형성하고 있는 Calcium 및 Magnesium 과 Copper-PHB 와 Calcium 및 Magnesium-maleate 를 각각 합성하였다. 그중 Calcium-PHB 를 Ethylene glycol과 혼합하여 MDI 와 반응시켜 고분자 주쇄에 금속을 함유하고 있는 이온성 Polyurethane 을 합성하고, 고분자 주쇄에 이온결합이 도입됨으로써 나타나는 고분자의 물리적 성질을 조사하였다. 금속의 함량증가함에 점도는 급격히 감소하였으며 용융점은 점차 감소함을 관찰할 수 있었다.
또 Calcium-maleate를 A.N과 공중합 시켜 고분자 측쇄에 금속염을 포함한 이온결합을 형성하고 있는 고분자를 합성하고, 고분자의 측쇄에 금속이 도입됨으로 나타나는 고분자의 대수점도 및 용융점의 변화를 조사하였다.
측쇄에 이온결합이 도입됨으로써 점도는 급격히 증가하였으며 용융점은 점차 낮아지는 현상을 관찰할 수 있었다.
Divalent metal-PHB와 Divalent metal-Maleate를 5% 이내로 고분자에 도입시켰을 때 고분자 자체의 기계적 성질의 변화는 별로 초래하지 않고 금속이나 이온결합으로 인한 전기전도성, 흡습성, 난연성을 지닌 고분자를 합성할 수 있을 것으로 전망된다.