Transport phenomena of a series of aqueous amides across the poly (2-hydroxyl ethyl methacrylate) (p-HEMA) hydroxyl membrane were studied.
Hydrogel membrane were synthesized by the solution polymerization of 2-hydroxyethyl methacrylate(HEMA) in the presence of crosslinking agent tetraethylene glycol dimethacrylate(TEGDMA).
By changing the crosslinker contents, four group of membranes were synthesized. Diffusion data of solutes were obtained for each group of membranes.
A Leonard-Blumle cell was used throughout the experiments. The overall permeability, the distribution coefficient, the solution volume, the membrane wet thickness and wet area were measured. From these experimental values, the diffusion coefficients of solutes through membranes were calculated.
The concentration measurement were carried out by differential refractometry at 546 nm wavelength.
Diffusion data were interpreted in terms of the extent of interaction between solute and membrane matrix. It was assumed that there are pores which are the water containing region in the hydrogel.
Hydrogen bonding ability and size effect were considered as the factors to affect the diffusion of nonelectrolite solutes.
A cylindrical treatment of the configuration of small molecules in membranes was proposed.
It was observed that in the membrane of low crosslinker content, the molecular size was the important factor in diffusion, while with increase of crosslinker content, hydrogen bonding effect also become important.
Poly(2-hydroxyethyl methacrylate) 수화겔 속에서의 이동현상을 일련의 아마이드 수용액에 대하여 연구했다. 수화겔 막은 2-hydroxethylmethacrylate 를 가교제인 Tetra ethylene glycol dimethacrylate (TEGDMA) 와 함께 용액 중합방법에 의해 제조했다. 가교제의 성분비에 따라 4종류의 막을 만들고 각 종류의 막에 대하여 용질의 확산 계수를 구했다.
전 실험을 통해 Leonard-Blunle 확산 용기를 사용하였으며 전 투과계수 분배계수 용액의 부피 막의 두께와 면적을 측정하였다. 이 실험값들로 부터 막에서의 확산계수를 계산하였다. 용액의 농도는 546 nm에서 급절계를 사용하여 측정했다.
확산 실험결과는 용질과 막의 상호작용과 hydrogel 에서 물을 포함하는 부분이 미세공처럼 작용한다는 관점에서 생각됐다. 수소결합과 분자크기가 비전해질의 확산에 영향을 주는 것으로 생각했다. 그리고 막내에서의 작은 분자의 배열이 원동형 모형임이 제안되었다. 즉 가교 결합의 정도가 낮은 막에서는 분자크기가 확산에 크게 영향을 주지만 가교 결합의 정도가 증가할수록 수소 결합 효과가 역시 커짐이 관찰되었다.