The anionic polymerization of ε-caprolactam via $CS_2$/KOH catalysis was carried out under various conditions.
The inherent viscosity and percent conversion of the polymers were determined.
It was observed that the percent conversion was increased as an increasing concentration of catalyst and initiator.
The percent conversion was relatively low at low temperature and the highest percent conversion was obtained at temperature between 130℃ to 155℃ with any $CS_2$/KOH mole ratio.
$CS_2/KOH$ catalysis를 이용해서 ε-caprolactam의 음이온중합을 시키고 percent conversion과 점도를 측정하였다.
80℃, 105℃의 비교적 낮은 온도에서는 $CS_2/KOH$ mole ratio가 0.5일 때 percent conversion이 가장 높았으며 또 KOH의 당량에 비례하여 percent conversion도 증가하였다.
그러나 130℃, 155℃로 중합온도를 상승함에 따라 $CS_2/KOH$ mole ratio 와 KOH 양에는 크게 관계없이 높은 percent conversion 을 얻을 수 있었다.
그리고 30分정도의 짧은 중합시간으로도 80% 이상의 높은 percent conversion 을 얻을 수 있었다.