We demonstrated the first foldable Ag nanowires loudspeaker on paper by using fast, easy, and cheap direct vacuum filtration method. The foldable Ag nanowires loudspeaker (4.2cm x 4cm) had a resistance of 20~30Ω and it could be folded from -180° to 180°. The sound from flat Ag nanowires loudspeaker (4.2cm x 4cm) was mainly propagated on the axis ±30° at 2kHz and ±5° at 20kHz. SPL of concave-shaped and convex-shaped foldable Ag nanowires loudspeaker was measured as a function of folding angle and the experimental results were explained by directivity simulation using theoretical model. SPL of repetitive concave and convex-shaped foldable Ag nanowires loudspeaker was measured as a function of input power, folding angle, and directivity. The flat and repetitive concave and convex-shaped foldable Ag nanowires loudspeaker had a similar sound-emitting characteristics. Our foldable Ag nanowires loudspeaker maintained uniform acoustic performance even if folding and unfolding cycle was repeated. Our foldable device had advantages in portability and space-saving, and it could be utilized in portable loudspeaker, touch panel, and paper-based media.
우리는 빠르고, 쉬우며, 값싼 직접 진공 여과방법을 이용하여 접을 수 있는 은 나노와이어 스피커를 제작하였다. 접을 수 있는 은 나노와이어 스피커 (4.2cm x 4cm)는 20~30Ω의 가지고, -180°에서 180° 까지 접을 수 있다. 평평한 형태의 은 나노와이어 스피커(4.2cm x 4cm)으로 부터 방사되는 소리는 2kHz 하에서 축 방향으로부터 ±30° 방향으로 주로 진행하고, 20kHz 하에서 축 방향으로부터 ±5° 방향으로 주로 진행한다. 오목한 형태와 볼록한 형태의 접을 수 있는 은 나노와이어 스피커의 접는 각도에 따른 음압레벨을 측정하였고, 실험결과는 이론적 모델을 이용한 시뮬레이션 결과와 일치했다. 반복적인 오목 및 볼록한 형태의 접을 수 있는 은 나노와이어 스피커의 인가 전력, 접는 각도, 소리 방사 방향에 따른 음압레벨을 측정하였다. 평평한 형태와 반복적인 오목 및 볼록한 형태의 접을 수 있는 은 나노와이어 스피커는 유사한 소리 방사 특성을 보였다. 우리의 접을 수 있는 은 나노와이어 스피커는 접고 펴는 동작을 반복해도 일정한 음향 성능을 보였다. 이 장치는 휴대성과 공간활동에 있어서 큰 이점을 가지고 있기 때문에 휴대용 스피커, 터치패널, 종이를 기반으로 한 매체에 응용 가능하다.