The effect of ECAE(equal channel angular extrusion)-processing on the thermo-mechanical properties of Ti-34.06wt.%Nb-0.14wt.%O and Ti-38.26wt.%Nb-0.14wt.%O shape memory alloys was studied by measuring the tensile stress-strain curve at various temperatures and using DSC, X-ray diffraction, and TEM. An ultra fine grain structure was developed by ECAE severe plastic deformation and by the formation of α(alpha)-particles on grain boundaries, which was facilitated by 0.14 weight percent oxygen. A severe grain refinement led to a large decrease of Ms from 216 ºC to 106 ºC. Furthermore, the elimination of oxygen in the matrix by α-particles led to an abrupt decrease of the stress for reorienting the martensite variants and stress for inducing martensite to an increase in the transformation strain. Subsequent ω(omega)-aging treatment further stabilized the β(beta)-phase at room temperature to show a superelastic property at Ti-34.06wt.%Nb-0.14wt.%O alloy.
Ti-34.06wt.%Nb-0.14wt.%O와 Ti-38.26wt.%Nb-0.14wt.%O 형상기억합금의 열기계적 특성에 대한 등통로각 압출의 효과에 대해 연구하였다. 등통로각 압출 가공한 두 합금은 후속 열처리로 목적에 따라 어닐링처리와 에이징 처리를 실시하였다. 가공한 시편은 인장시험을 여러 온도에서 실시하여 인장 변형 곡선을 얻고, DSC, XRD, TEM 분석을 이용해 결과를 해석하였다. 두 합금은 강 소성 가공 법인 등통로각 압출가공으로 인해 초 미세 결정립 구조가 발달한다. 동시에 기지에 포함된 0.14wt.%의 산소는 합금 내에서 알파상의 석출을 촉진시켜 알파상이 결정립계에 형성되게 한다. 등통로각 압출 가공한 뒤 어닐링 한 Ti-34.06wt.%Nb-0.14wt.%O 시편에서는 결정립이 현저히 미세화되고 이로 인해 마르텐사이트 변태 개시 온도가 216C에서 106C로 낮아졌다. 두 합금에서 알파상이 기지의 산소를 고용하여 기지의 산소가 줄어들어 마르텐사이트 재배열과 응력 유기 마르텐사이트 변태에 필요한 응력이 급격히 낮아지게 된다. 등통로각 압출 가공 후 어닐링 처리한 뒤 추가적으로 에이징 처리한 Ti-34.06wt.%Nb-0.14wt.%O 시편에서는 오메가상이 형성되어 베타상이 더욱 안정화되고 상온에서 초탄성 효과가 나타나게 된다.