Polyfluorene derivatives, PFDTPAs, including a triphenylamine moiety as a side chain were synthesized through Ni(0) mediated random copolymerization using fluorene and triphenylamine substituted phenyl monomers. All synthesized copolymers exhibited the similar absorption and photoluminescence (PL) maxima at about 388 nm and 414 nm in $CHCl_3$ solution, respectively. The maxima of the absorption and PL emission on the polymer films were appeared at ca. 381 nm and 474 nm, respectively. Polymer light-emitting diode (LED) devices were fabricated as an ITO/PEDOT/polymer (PFDTPA)/LiF/Al configuration. The electroluminescence (EL) emission maxima of the copolymers were gradually shifted to the long wavelength regions and EL quantum efficiencies of the PFDTPAs increased as the triphenylamine ratio increases. On the other hand, the threshold voltages of PFDTPAs LED devices were decreased, and brightness was increased as the content of triphenylamine moiety increases.
니켈(0)을 촉매로 하는 야마모토 반응을 이용하여, 정공 이동 물질로 이용되는 트리페닐아민을 포함하는 단분자와 플루오렌을 이용하여 다양한 비율의 PFDTPA 공중합체를 합성하였다. 이렇게 합성된 고분자들은 1H-NMR, 광 흡수 특성, 광 발광 특성, 전기발광 특성 등을 통해서 물성을 조사하였다. 또한 합성된 고분자들은 클로로포름, 테트라하이드로퓨란, 1,2-다이클로로에탄과 같은 일반적인 유기 용매에 잘 녹고 400℃ 까지 좋은 열안정성을 보였다. 고분자들의 분자량은 수평균 분자량이 20,100 에서 60,700을 그리고 무게 평균 분자량은 54,700 에서 193,800 으로 트리페닐아민이 적게 들어간 폴리머일수록 분자량은 높았다. 합성된 고분자들의 유리전이온도는 트리페닐아민이 많이 들어갈수록 높게 나타났다. 공중합체들은 약 380 nm 에서 최대 흡수 파장을 보였다. 그리고 트리페닐아민의 비율에 관계없이 약 500 nm 정도로 PDHF 보다 더 장파장쪽에서 빛발광 스펙트럼을 보였다. 전기 발광 소자는 ITO 위에 PEDOT 을 스핀 코팅한 후, 다시 그 위에 고분자를 스핀 코팅하고 LiF 와 Al 을 진공증착하여 제작하였다. 전기 발광 스펙트럼에서는 빛 발광 스펙트럼과는 달리 트리페닐아민 비율이 높을수록 장파장쪽으로 진행되며 PFDTPA10 에서는 백색광에 가까운 빛을 보였다. 또한 트리페닐아민 비율이 높아질수록 구동전압이 상당히 낮아지는 현상을 보였고, 발광 휘도에서도 향상된 현상을 보였다.