An investigation was carried out to predict two dimensional fillet geometry in aluminum dip brazing, and selected some parameters those could indicate a quality. An analytical method was used to predict a fillet geometry, considering surface tension forces and variations of gravitational directions. Performed dip brazing experiments for T-shaped specimens, for several process variables, such as preheating time, preheating temperature, brazing time, brazing temperature, quenching time and gravitation. For those variables, three parameters were selected to evaluate a quality of a brazed joint. They are tensile strength, surface roughness and surface hardness. Also a cross -section examination was carried out to observe a microstructure inside a fillet joint, and examined the effect of microstructure on the tensile strength and surface hardness. As a result, prediction of a fillet geometry was verified by experimental results, and proposed appropriate brazing conditions for specified brazing results.
알루미늄 딥 브레이징에서 2차원 필릿 형상을 예측하기 위한 연구를 수행하고 전반적인 접합 품질을 예측하기 위하여 적절한 변수들을 선정하였다. 필릿 형상의 예측은 표면장력과 중력 방향의 변화를 고려하여 해석적 방법으로 수행하였다. 딥 브레이징 실험은 T자 형태의 시편에 대하여 예열시간, 예열온도, 브레이징 시간, 브레이징 온도, 담금질 시간, 그리고 중력 방향을 변화시켜 가면서 실험을 수행하였다. 이러한 공정변수들의 변화에 대하여, 품질을 나타낼 수 있는 세 가지 변수로서 접합부 인장강도, 표면거칠기, 표면경도를 선정하여 그 결과를 알아보았고, 또한 접합부 단면을 검사하여 미세구조를 조사함으로써 미세구조가 결과에 미치는 영향을 알아보았다. 또한, 해석적 방법으로 예측된 필릿 형상을 실험 결과와 비교하여 거의일치 하는 결과를 얻었으며, 선택한 품질 항목에 대한 최적의 브레이징 조건을 제시하였다.