The Ball milling of leady oxide was proposed and applied to the control of the electrochemical activity of positive electrode in lead acid battery. The particle sizes, cystalline phases, chemical compositions, morphologies and BET surface areas of the produced particles and electrods were investigated by XRD, centrifugal particle size analyzer, SEM. Electrochemical activity of the modified electrodes was determined by measuring the discharging capacity of unit cell by cyclic voltametry.
The submicron size leady oxides(0.5㎛) were produced by the ball milling of leady oxide, and the crystalline size of this particles were decreased to 15 nano meter. The modified leady oxide have high nonuniform strain and surface area.
The active material of positive electrodes, produced by milled leady oxide, have high BET surface area. The micro pore ratio and $αPbO_2/β-PbO_2$ were increased by modification. The electrochemical activity of modified electrodes, however, slightly lower when discharging current density is low.
연분의 볼밀링이 연축전지 양극재료의 전기화학적 특성을 조절하는 데 제안되었다. 볼밀링을 통하여 제조된 연분과 전극의 입도, 결정상, 화학상과 비표면적등이 관찰되었으며,제조된 전극의 방전특성이 측정되었다. 실험으로 부터,볼밀링이 연분의 입자크기를 서브미크론 이하로 감소시키며,결정자 크기도 나노미터사이즈로 감소시킴을 알 수 있었다. 이 때의 연분은 높은 불균일변형율과 비표면적을 나타내었다. 이로 부터 제조된 양극활물질은 높은 비표면적과 다공도를 보이며, 미세기공의 비율이 증가하고 결정상의 비가 변화함을 알 수 있었다. 그러나, 이러한 전극들은 낮은 방전전류 밀도에서는 낮은 방전용량을 나타내었다.